Tribological and Antimicrobial Properties of Two-Component Self-Assembled Monolayers Deposited on Ti-Incorporated Carbon Coatings.

In this work, Ti-incorporated carbon coatings were used as substrates for modification with one- and two-component self-assembled monolayers of organosilane compounds using a polydimethylsiloxane (PDMS) stamp. This enabled the selective functionalization of surfaces with micrometric dimensions. The topography of the modified surfaces was defined using an atomic force microscope (AFM). The effectiveness of the modification was confirmed by measurements of the water contact angle and surface free energy using the Oss and Good method. Using a T-23 microtribometer with counterparts in the shape of balls that were made of steel, silicon nitride (Si3N4), and zirconium dioxide (ZrO2), the tribological properties of the obtained coatings were tested. These investigations showed that modification by using a PDMS stamp makes it possible to produce two-component ultrathin silane layers on Ti-containing carbon substrates. Two-component organosilane layers had higher hydrophobicity, a lower friction coefficient, and a smaller width of wear tracks than the one-component analogs. It was also found that the work of adhesion of the created surfaces had a significant influence on the value of the friction coefficient and the percentage value of the growth inhibition of bacteria.

Constant Magnetic Field as a Tool for Modification of the Properties of Polymer Composites with Silicone Rubber Matrix.

The aim of this research was to obtain new polymer composites with a silicone rubber matrix, having favorable mechanical and functional properties. They contained admixtures in the amount of 10% by weight of expanded graphite (EG) or birch bark (BB). Additionally, some composites contained magnetic particles in the form of carbonyl iron in the amount of 20% by weight. The tensile strength, water absorption, frost resistance, surface contact angle, and free surface energy were examined. Microscopic images were taken using the SEM method and the content of some elements in selected microareas was determined using the EDXS method. In the study, a constant magnetic field with magnetic induction B was used, by means of which the properties and structure of polymer composites were modified. Scientific research in the field of polymers is the driving force behind the progress of civilization. Smart materials are able to respond to external stimuli, such as magnetic fields, with significant changes in their properties. The magnetic field affects not only chemical reactions, but also the crystallographic structure and physicochemical properties of the final products. Owing to their unique properties, such materials can be used in the space industry, automotive industry, or electrical engineering.

Corrosion Resistance of Titanium Dental Implant Abutments: Comparative Analysis and Surface Characterization.

Metals subjected to the oral environment are prone to corrosion over time and this can be harmful. Metallic restoration components such as dental subgingival implant abutments are exposed to pH changes and different ions while in contact with saliva. The aim of the study was to evaluate the corrosion resistance of titanium dental implant abutments and to compare and contrast the surface characteristics of these alloys before and after corrosion. The corrosion examination (Ecorr, jcorr, OCP, polarization curve) of two implant abutments (TiDesign EV, Astra Tech, Dentsply, York, PA, USA; Individual Titanium Abutment, Apollo Implants Components, Pabianice, Poland) was performed in 0.9% NaCl and 5% HCl. Moreover, specimens were investigated using SEM-EDS before and after the corrosion test. The value of jcorr in NaCl was higher for Astra (34.2 × 10-8 ± 2.5 × 10-8 A/cm2) than for Apollo (8.8 × 10-8 ± 2.5 × 10-8 A/cm2). Whereas, in HCl, the opposite relationship was observed (Astra 2.9 × 10-4 ± 0.8 × 10-4 A/cm2 and Apollo 62.7 × 10-4 ± 9.3 × 10-4 A/cm2). An average reactive anodic current density in NaCl for Astra amounted up to ~0.2 × 10-5-1.5 × 10-5 A/cm2, while for Apollo-up to ~3.3-9.7 × 10-7 A/cm2. The composition of both alloys after corrosion in NaCl demonstrated some changes: a decrease in the Ti, and Al and an increase in oxygen content. Hence, both alloys after corrosion in HCl demonstrated some minor changes in the elemental composition. Based on the results it can be concluded that: 1. Astra and Apollo abutments revealed good corrosion resistance and a passivation layer on the surface. 2. Apollo abutments exhibited better corrosion resistance in a neutral environment, suggesting that Astra abutments were found to be more resistant to corrosion in an acidic medium.

The Use of Extraction on C18-Silica-Modified Magnetic Nanoparticles for the Determination of Ciprofloxacin and Ofloxacin in Meat Tissues.

A simple, fast, and low-cost method of extraction using magnetic nanoparticles was developed for sample preparation in the determination of ciprofloxacin and ofloxacin in meat tissues with the use of capillary electrophoresis. This study is the first utilization of silica-coated magnetic nanoparticles with attached C18 chains to extract fluoroquinolones from meat tissues. This method is therefore characterized by a very simple sample preparation procedure, but on the other hand, by satisfactory precision and accuracy. Magnetic nanoparticles with an appropriately modified surface were placed in an Eppendorf tube, then conditioned with methanol, next rinsed with water and, finally, a homogenized tissue sample was added. At the neutral pH of the sample solution, these compounds do not have a charge and are able to adsorb on the modified particles. After extraction, the nanoparticles were dried and, then, desorption of analytes was conducted with the use of a mixture of 0.1 mol/L HCl and acetonitrile (1:1). This approach made it possible to purify the sample matrix and to obtain satisfactory LOQ levels for the method using the CE technique with UV-Vis detection. In this method, the LOD and LOQ values for both analytes were 0.04 nmol/g tissue and 0.15 nmol/g tissue, respectively. The calibration curves were linear in the entire concentration range, and the accuracy and the recovery of the method were at the satisfactory levels. The square value of the linear correlation coefficients (R2) for Cpx and Ofx were 0.9995 and 0.9992, respectively. The precision value of the method was within the range of 3-11% and accuracy was in the range of 93-110%.

Micro-CT Evaluation of Microgaps at Implant-Abutment Connection.

The assessment of microgaps at the implant-abutment interface is an important factor that may influence clinical success. Thus, the aim of this study was to evaluate the size of microgaps between prefabricated and customised abutments (Astra Tech, Dentsply, York, PA, USA; Apollo Implants Components, Pabianice, Poland) mounted on a standard implant. The measurement of the microgap was performed using micro-computed tomography (MCT). Due to 15-degree rotation of samples, 24 microsections were obtained. Scans were performed at four levels established at the interface between the abutment and the implant neck. Moreover, the volume of the microgap was evaluated. The size of the microgap at all measured levels varied from 0.1 to 3.7 µm for Astra and from 0.1 to 4.9 µm for Apollo (p > 0.05). Moreover, 90% of the Astra specimens and 70% of the Apollo specimens did not exhibit any microgaps. The highest mean values of microgap size for both groups were detected at the lowest portion of the abutment (p > 0.05). Additionally, the average microgap volume was greater for Apollo than for Astra (p > 0.05). It can be concluded that most samples did not exhibit any microgaps. Furthermore, the linear and volumetric dimensions of microgaps observed at the interface between Apollo or Astra abutments and Astra implants were comparable. Additionally, all tested components presented microgaps (if any) that were clinically acceptable. However, the microgap size of the Apollo abutment was higher and more variable than that of the Astra one.

Insights into the physical and chemical properties of struvite crystal surfaces in terms of the effectiveness of bacterial adhesion.

In this paper, we present the results of research on the physicochemical properties of two selected faces of the struvite crystal, which is the main component of infectious urinary stones. Two main faces, (001) and ([Formula: see text]), ending the c-axis, were selected for the study. These faces are not related by symmetry relations, which means, among other things, that they should have a different atomic structure, which was confirmed experimentally. In addition, the studies show that the tested surfaces have hydrophilic properties, however, the ([Formula: see text]) face is more hydrophilic compared to the (001) face. The physicochemical properties of the crystal as a whole, as well as the physicochemical properties of these faces influence the magnitude of adhesion. The adhesive force in both water and artificial urine is greater for face ([Formula: see text]) compared to face (001). The assessment of the adhesion of Proteus mirabilis bacteria in artificial urine also shows that the adhesion is greater for face ([Formula: see text]) than for face (001). The adhesion of bacteria to the examined faces of the struvite crystal, and in particular the increased adhesion of bacteria to the face ([Formula: see text]), may be the first stage of biofilm formation, which may result in a high rate of recurrence of infectious urinary stones after treatment.

Tests of Physicochemical and Mechanical Strength Properties of Polymer Composites on an Epoxy Resin Matrix, Modified by a Constant Magnetic Field.

The aim of the research presented in the paper was to obtain new polymer composites with strong functional properties on the Epidian 5 epoxy resin matrix. The polymer composites contained admixtures of expanded graphite, powder graphite, birch bark containing botulin, and yellow dextrin in set amounts of 20% by weight. Their various mechanical parameters and physicochemical properties were investigated. The research involved determining the effect of a constant magnetic field with magnetic induction B, under the influence of which the parameters and properties of polymer composites have been changed. For example, in a constant magnetic field with an induction of B = 0.5 T there was an increase in the hardness of the composite with an admixture of birch bark from 24.01 to 26.96 N/mm2 (12.3%), or in the composite with the addition of yellow dextrin from 26.12 to 29.93 N/mm2 (14.6%). It was also found, for example, that the water absorption of the resin itself decreased from 0.18% to 0.13%, and the composite with graphite powder from 0.48% to 0.46%. Changes in these parameters, often beneficial, may be important in terms of potential application of those new materials in industry as alternatives.

Changes in the Laser-Processed Ti6Al4V Titanium Alloy Surface Observed by Using Raman Spectroscopy.

This works reports on the effects of treating the surface of Ti6Al4V titanium alloy samples with a laser with a wavelength of 1064 nm, operating in a pulsed and continuous mode. The obtained surfaces with different roughness, complexity and wettability were examined by Raman spectroscopy in order to recognize the presence of titanium oxides on the functionalized surface. The layer of titanium oxides on the surface with the identified rutile phase obtained by laser treatment in the continuous wave mode is a reason for a hydrophobic surface that appeared 50 days after the treatment process. In the case of the surface obtained by the pulsed laser process, only local points at which the Raman bands attributed to the metastable phases anatase and brookite of TiO2 can be identified. In this treatment process, complete surface hydrophilicity was observed during 29 days after the functionalization process (maximal contact angle observed during this time was 68.4 deg). For some functionalization processes of different parameters, the contact angle remained immeasurable until 119 days after the functionalization process. In summary, Raman spectroscopy identifies surface changes of Ti6Al4V after laser processing.

Modification of the Properties of Polymer Composites in a Constant Magnetic Field Environment.

In this paper, polymer composites based on polylactide (PLA) and epoxy resin (Epidian 5) were studied in terms of the influence of magnetic induction on their changes in physicochemical properties. The composites contained admixtures in the form of magnetite (Fe3O4) and crystalline cellulose (Avicel PH-1010) in the amount of 10%, 20%, and 30% by weight and starch in the amount of 10%. The admixtures of cellulose and starch were intended to result in the composites becoming biodegradable biopolymers to some extent. Changes in physical and chemical properties due to the impact of a constant magnetic field with a magnetic induction value B = 0.5 T were observed. The changes were observed during tests of tensile strength, bending, impact strength, water absorbency, frost resistance, chemical resistance to acids and bases, as well as through SEM microscopy and with studies of the composition of the composites that use the EDS method and of their structure with the XRD method. Based on the obtained results, it was found that the magnetic induction value changes the properties of composites. This therefore acts as one method of receiving new alternative materials, the degradation of which in the environment would take far less time.

Key Properties of a Bioactive Ag-SiO2/TiO2 Coating on NiTi Shape Memory Alloy as Necessary at the Development of a New Class of Biomedical Materials.

Recent years have seen the dynamic development of methods for functionalizing the surface of implants using biomaterials that can mimic the physical and mechanical nature of native tissue, prevent the formation of bacterial biofilm, promote osteoconduction, and have the ability to sustain cell proliferation. One of the concepts for achieving this goal, which is presented in this work, is to functionalize the surface of NiTi shape memory alloy by an atypical glass-like nanocomposite that consists of SiO2-TiO2 with silver nanoparticles. However, determining the potential medical uses of bio(nano)coating prepared in this way requires an analysis of its surface roughness, tribology, or wettability, especially in the context of the commonly used reference coat-forming hydroxyapatite (HAp). According to our results, the surface roughness ranged between (112 ± 3) nm (Ag-SiO2)-(141 ± 5) nm (HAp), the water contact angle was in the range (74.8 ± 1.6)° (Ag-SiO2)-(70.6 ± 1.2)° (HAp), while the surface free energy was in the range of 45.4 mJ/m2 (Ag-SiO2)-46.8 mJ/m2 (HAp). The adhesive force and friction coefficient were determined to be 1.04 (Ag-SiO2)-1.14 (HAp) and 0.247 ± 0.012 (Ag-SiO2) and 0.397 ± 0.034 (HAp), respectively. The chemical data showed that the release of the metal, mainly Ni from the covered NiTi substrate or Ag from Ag-SiO2 coating had a negligible effect. It was revealed that the NiTi alloy that was coated with Ag-SiO2 did not favor the formation of E. coli or S. aureus biofilm compared to the HAp-coated alloy. Moreover, both approaches to surface functionalization indicated good viability of the normal human dermal fibroblast and osteoblast cells and confirmed the high osteoconductive features of the biomaterial. The similarities of both types of coat-forming materials indicate an excellent potential of the silver-silica composite as a new material for the functionalization of the surface of a biomaterial and the development of a new type of functionalized implants.

Comparison of the Physicochemical Properties of Carboxylic and Phosphonic Acid Self-Assembled Monolayers Created on a Ti-6Al-4V Substrate.

This study compared the tribological properties in nano- and millinewton load ranges of Ti­6Al-4V surfaces that were modified using self-assembled monolayers (SAMs) of carboxylic and phosphonic acids. The effectiveness of the creation of SAMs with the use of the liquid phase deposition (LPD) technique was monitored by the contact angle measurement, the surface free energy (SFE) calculation, X-ray photoelectron spectroscopy (XPS), and Fourier-transform infrared spectroscopy (FTIR) measurements. The obtained results indicated that more stable and well-ordered layers, which were characterized by the lowest values of the coefficient of friction, adhesion, and wear rate, were obtained using phosphonic acid as a surface modifier. Based on the obtained results, it was found that the Ti-6Al-4V alloy modified by phosphonic acid would be the most advantageous for practical applications, especially in micro- and nanoelectromechanical systems (MEMS/NEMS).

The Effect of Physicochemical Properties of Perfluoroalkylsilanes Solutions on Microtribological Features of Created Self-Assembled Monolayers.

The presented article shows the influence of concentration of perfluoroalkylsilanes in solutions on tribological properties of self-assembled monolayers (SAMs) deposited on three surfaces with different silicon content in the millinewton load range. The SAMs were created using the liquid phase deposition (LPD) method with 1H, 1H, 2H, 2H-perfluorodecyltrichlorosilane (FDTS) and (3, 3, 3-trifluoropropyl) trichlorosilane (FPTS) solutions, for which viscosity and surface tension were estimated. Deposited layers were analyzed in terms of thickness, coverage, wettability, structure and coefficient of friction. The obtained results demonstrated that SAMs created on the silicon-incorporated diamond-like carbon (Si-DLC) coatings possess the best microtribological properties. Systems composed of perfluoroalkylsilane SAM structures deposited on Si-DLC coatings are highly promising candidates as material for microelectromechanical applications.

Impact of Perfluoro and Alkylphosphonic Self-Assembled Monolayers on Tribological and Antimicrobial Properties of Ti-DLC Coatings.

The diamond-like carbon (DLC) coatings containing 1.6%, 5.3% and 9.4 at.% of Ti deposited by the radio frequency plasma enhanced chemical vapor deposition (RF PECVD) method on the silicon substrate were modified by n-decylphosphonic acid (DP) and 1H, 1H, 2H and 2H-perfluorodecylphosphonic acid (PFDP). The presence of perfluoro and alkylphosphonic self-assembled monolayers prepared by the liquid phase deposition (LPD) technique was confirmed by Fourier transform infrared spectroscopy (FTIR). It was shown that DP and PFDP monolayers on the surface of titanium incorporated diamond-like carbon (Ti-DLC) coatings had a huge influence on their wettability, friction properties, stability under phosphate- and tris-buffered saline solutions and on antimicrobial activity. It was also found that the dispersive component of surface free energy (SFE) had a significant influence on the value of the friction coefficient and the percentage value of the growth inhibition of bacteria. The dispersive component of SFE caused a reduction in the growth of bacteria and the friction coefficient in mili- and nano-newton load range. Additionally, both self-assembled monolayers prepared on Ti-DLC coatings strongly reduced bacterial activity by up to 95% compared to the control sample.